S9.5 - GF - Primer Surfacer



S 9.5 GF - Primer Surfacer

S 9.5.1 Standoflex(R) 2K Plastic Primer Surfacer
S 9.5.1.1 Processing

S 9.5.2 Standox(R) 2K Nonstop Primer Filler
S 9.5.2.1 Application as a wet-on-wet filler
S 9.5.2.2 Working with sanding filler

S 9.5.3 Standohyd(R) 1K Primer Surfacer
S 9.5.3.1 Processing

S 9.5.4 Standox(R) EP Primer Surfacer
S 9.5.4.1 Application as a wet-on-wet filler
S 9.5.4.2 Working with sanding filler

S 9.5.1 Standoflex(R) 2K Plastic Primer Surfacer







WARNING: -> 2 "Safety regulations" and read the product-specific safety instructions on the container labels.

Description:
- 2K Plastic Primer Surfacer

Properties:
- Adheres to all paintable plastic parts on outside of passenger vehicles
- Can be painted over or sanded wet-on-wet
- Easy to handle
- Efficient procedure
- Ready to spray once hardener is added

Base surfaces:
- PC
- PP
- PP/EPDM
- PVC
- ABS and SAN
- UP- GF (formerly GfK)
- PU-RIM
- RTPU
- PUR
- PA
- PPO
- PBTP
- Please note base surface pre-treatment instructions:
-> S 6.1
-> S 9.2.2

NOTE:
- Raw material base: Special polymers
- Flash point: 23° C/73.4° F
- Spec. weight: 1.20 g/cm3
- Solid content: 53.8-55.2% weight/36.9-37.9% vol.
- Theoretical yield: 7.8 m2/ltr. with a dry coat thickness of 30 microns
- Only use specified Standoflex(R) 2K Plastic Hardener
- Do not store Standoflex(R) 2K Plastic Hardener below +10° C
- Clean equipment after use with cleaning thinner

VOC value:
- 539 g/l

NOTE:
- PE (polyethylene) and POM (polyoxymethylene) cannot be painted manually.

S 9.5.1.1 Processing







S 9.5.2 Standox(R) 2K Nonstop Primer Filler







WARNING: -> 2 "Safety regulations" and read the product-specific safety instructions on the container labels.

Description:
- Universal 2K wet-on-wet and sanding filler

Properties:
- Wide range of uses
- Very good paint texture
- Chromate-free

Base surfaces:
- Hardened paintwork, sanded
- Polyester products, sanded
- Cleaned sheet steel, sanded
- Factory primer and KTL, sanded
- Aluminum and galvanized base surfaces must be pre-primed with Standox(R) Etching Adhesion Primer
- Please note base surface pre-treatment instructions:
-> S 5.1
-> S 6.1
-> S 9.2.2

NOTE:
- Raw material base: Acrylic polyurethane, corrosion inhibition pigments
- Flash point: 24° C/75.2° F
- Spec. weight: 1.55 g/cm3
- Solid content: 70.3% weight/47.7% vol.
- Theoretical yield as wet-on-wet filler: 13.9 m2/ltr. with a dry coat thickness of 30 microns
- Theoretical yield: 5.2 m2/ltr. with a dry coat thickness of 80 microns
- Clean equipment after use with cleaning thinner

VOC value:
- 460 g/l

NOTE:
- VOC-compliant when used as a sanding filler with up to 8% thinner added.
- Use with Standox(R) 2K Plasticizer (new) on primed plastics.

WARNING: 2K paints react with moisture. All work equipment, mixing vessels, etc. must therefore be completely water-free.

S 9.5.2.1 Application as a wet-on-wet filler







S 9.5.2.2 Working with sanding filler







S 9.5.3 Standohyd(R) 1K Primer Surfacer







WARNING: -> 2 "Safety regulations" and read the product-specific safety instructions on the container labels.

Description:
- Water-dilutable Standohyd(R) 1K Primer Surfacer

Properties:
- Organic solvent content: less than 10%
- Use mainly for minor repair jobs
- For solvent-reduced paint finishes
- Wide range of uses
- No identifying features

Base surfaces:
- Hardened paintwork, sanded
- Sheet steel, sanded
- Aluminum, sanded
- Galvanized steel, sanded
- Polyester products, sanded
- KTL, sanded
- Please note base surface pre-treatment instructions:
-> S 5.1
-> S 6.1
-> S 9.2.2

Note:
- Raw material base: Special polymers that can be diluted in water
- Flash point: 80° C/176.0° F
- Spec. weight: 1.43 g/cm3
- Solid content: 60.0% weight/41.9% vol.
- Theoretical yield: 8.4 m2/ltr. with a dry coat thickness of 50 microns
- Storage: Unopened original containers can be stored for 12 months at 20° C. Do not store at below 5° C.
- Rinse equipment before and after use with Standohyd(R) Demineralized Water, then clean again with cleaning thinner

VOC value:
- 93 g/l

NOTE:
- Work materials must be suitable for water-dilutable products; see manufacturer s specifications.
- Dispose of cleaning water correctly, not into sewerage systems.
- Collect left-overs from water-dilutable products separately from left-overs from conventional products.

S 9.5.3.1 Processing







S 9.5.4 Standox(R) EP Primer Surfacer







WARNING: -> 2 "Safety regulations" and read the product-specific safety instructions on the container labels.

Description:
- Universal 2K wet-on-wet and sanding filler

Properties:
- Wide range of uses
- Very good paint texture
- Chromate-free
- Good insulator

Base surfaces:
- Hardened paintwork, sanded
- Polyester products, sanded
- Cleaned sheet steel, sanded
- Factory primer and KTL, sanded
- Aluminum and galvanized base surfaces
- Fiber-reinforced plastic
- Please note base surface pre-treatment instructions:
-> S 5.1
-> S 6.1
-> S 9.2.2

NOTE:
- Raw material base: Epoxy resin, corrosion inhibition pigments
- Flash point: 28° C/82.4° F
- Spec. weight: 1.6 g/cm3
- Solid content: 73.8% weight/52.4% vol.
- Theoretical yield: 5.6 m2/ltr. with a dry coat thickness of 75 microns
- Clean equipment with cleaning thinner

VOC value:
- 420 g/l

NOTE:
- Do not use Standox(R) EP Primer Surfacer on acid primer.

S 9.5.4.1 Application as a wet-on-wet filler







S 9.5.4.2 Working with sanding filler